Babbitt Alloy Welding Wire

Manufacturing all kinds of large generators, turbines, turbine, steam turbine, compressor, turbine pump, internal combustion engine oil machinery, chemical machinery, metal roll, cement ball mill, pulp mixing machine, drying machine large rotating equipment such as bearing, shaft sleeve, the key of the bushing material.
Product is suitable for using TIG or MIG welding technology in the manufacture of sliding bearing, wear-resisting layer and matrix combined with high strength, high material utilization, effectively reduce the composition segregation, osteoporosis, and defects such as slag.
Product specifications: 1.2 mm - 4.0 mm Φ Φ
Products are mainly brand:, Sn8, Sn8 Sn4-4-4-8, Sn11-6
Product packaging: plastic tray, 10 kg/tray

Quantity:
























1515631758(1) 1515631738(1)
1515631791(1) 1515631871(1)




Instructions

   

  Manufacturing all kinds of large generators, turbines, turbine, steam turbine, compressor, turbine pump, internal combustion engine oil machinery, chemical machinery, metal roll, cement ball mill, pulp mixing machine, drying machine large rotating equipment such as bearing, shaft sleeve, the key of the bushing material.

  Product is suitable for using TIG or MIG welding technology in the manufacture of sliding bearing, wear-resisting layer and matrix combined with high strength, high material utilization, effectively reduce the composition segregation, osteoporosis, and defects such as slag.

   Product specifications: 1.2 mm - 4.0 mm Φ Φ

   Products are mainly brand:, Sn8, Sn8 Sn4-4-4-8, Sn11-6

   Product packaging: plastic tray, 10 kg/tray

Parameter


Product composition:

Brand
 
Composition wt%
Sn
Pb
Sb
Cu
Fe
As
Bi
Zn
Al
Cd
SnSb4Cu4
Allowance
0.35
4.0-5.0
4.0-5.0
0.06
0.10
0.08
0.005
0.005
0.05
SnSb8Cu4
Allowance
0.35
7.0-8.0
4.0-5.0
 
0.06
 
0.10
0.08
0.005
0.005
0.05
SnSb8Cu8
Allowance
0.35
7.5-8.5
7.5-8.5
0.08
0.10
0.08
0.005
0.005
0.05
SnSb11Cu6
Allowance
0.35
10.0-12.0
5.5-6.5
 
0.08
0.05
 
0.05
0.005
0.005
0.05
SnSb12Pb10Cu4
Allowance
9.0-11.0
11.0-13.0
2.5-5.0
0.08
0.10
 
0.08
0.005
0.005
0.05

Alloy as-cast performance:

Brand
ASTM Grade
Hardness
HB
Yield StrengthMpa
Compressive StrengthMPa
Density
g/cm3)
Melting Point
(℃)
SnSb4Cu4
1
≤17
≤30.3
≤88.6
7.34
223-371
SnSb8Cu4
2
≤24.5
≤42.0
≤102.7
7.39
241-354
SnSb8Cu8
3
≤27
≤45.5
≤121.3
7.46
240-442
SnSb11Cu6

≤27
≤51.7
≤132.6


SnSb12Pb10Cu4
4
≤29
≤51.7
≤129.3


Typical cladding performance:

Surfacing welding way
Bond strength (tensile)
Cladding speed

Machining Accuracy

Effectiveness (Thickness)

 
TIG
3000PSI(20.7MPa)
48 lbs /hr/100A
70%
MIG
3500PSI(24.1MPa)
65 lbs /hr/100A
70%

About rolls over superiorly

Relates rolls over superiorly

Contact : Xiaohua Shi
Moblie: 13962464998
Serves hot line: 0512-58907835
Tel: +86-512-58907836
Email: mkhmpr@163.com

Online inquires the disk

© Copyright  Jiangsu Goodroller Machinery Co., Ltd            
Website map    Jiangsu Goodroller Machinery Co., Ltd               Control entrance